Due to the introduction of Chromium (Cr), the internal stress of Titanium Aluminum Nitride (TiAlN) is significantly reduced and the impact resistance is improved.
Due to the introduction of Chromium (Cr), the internal stress of Titanium Aluminum Nitride (TiAlN) is significantly reduced and the impact resistance is improved.
Properties of Huinano-Titanium Aluminum Chromium Nitride aluminum-titanium (TiAlCrN) coatings
Film thickness: <=6um
Friction coefficient: <0.3
Film hardness: =<45GPa (~HV4500)
Maximum operating temperature: 1200°C
Film color: purplish gray
Process temperature: 400°C
Coating structure: nano monolayer/composite
Due to the introduction of Chromium (Cr), the internal stress of Titanium Aluminum Nitride (TiAlN) is significantly reduced and the impact resistance is improved. At the same time, the surface defects of the coating are significantly reduced and the temperature resistance is also improved.